Abstract
Al coating was deposited on 0Cr18Ni10Ti steel by magnetron sputtering, and then diffusing annealing at 950°C for 2h. The isothermal oxidation behaviors of the Al coating and 0Cr18Ni10Ti steel were tested at 900 °C for 24 h and 800 °C for 24 h using Thermo gravimetric analyzer. The morphology was studied by SEM, the phase composition was characterized by EDS. The result of isothermal oxidation test showed that isothermal oxidation resistance of Al coated steel is better than 0Cr18Ni10Ti steel at 900 °Cand 800 °C, due to continuous and compact Al2O3scales. Al clusters of particles appears on Al coated steel during deposition. The larger particles peeling off was observed at 900°C after 18h, due to thermal and growth stresses, while no spallation appeared at 800°C for 24h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.