Abstract
SiCf/SiC composites were annealed at 1300 °C for 5 h in argon and then fully cladded by LaMgAl11O19/Yb2Si2O7 (LMA/YbDS) thermal/environmental barrier coatings (T/EBCs). The annealed and coated system, directly-coated one and non-coated composites were isothermally oxidized at 1350 °C for 300 h. The oxidation resistance was estimated by strength retention rates. Compared to serious strength degradation in the non-coated composites, high strength retention rates were obtained for the coated ones, indicating LMA/YbDS provided effective protection for SiCf/SiC. Additionally, the annealed and coated system had higher strength retention rates than directly-coated one, resulting from weakened interfacial bonding strength between SiC matrix and fibers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.