High Temperature Oxidation Behavior of High Nitrogen Ferritic Steels

Abstract

Abstract For last half century the development of creep strength enhanced ferritic steels has been continued and presently ASME grades 91, 92 and 122 extremely stronger than conventional low alloy steels have extensively been used worldwide in high efficient power plants. However the use of these creep strength enhanced 9-12%Cr steels is limited to around 630°C or 650°C at maximum in terms of high temperature strength and oxidation resistance. Consequently the appearance of ferritic steels standing up to higher temperature of around 700°C to substitute of high strength austenitic steels is strongly desired. Under the state, the addition of high nitrogen to ferritic steels is attracting considerable attention because of improving high temperature strength and oxidation resistance of them. This work was done to evaluate the oxidation resistance of high nitrogen steels and to investigate the effect nitrogen and microstructure on oxidation resistance using 9-15%Cr steels with about 0.3% nitrogen manufactured by means of Pressurized Electro- Slag Remelting (PESR) method in comparison with ASME grades 91 and 122. As a result, high nitrogen ferritic steels showed excellent oxidation resistance comparing with nitrogen-free steels and ASME grades 91 and 122. The oxidation resistance of 9%Cr ferritic steels depends on the nitrogen content in the each steel. That is, the weight gain decreases with an increase in nitrogen content. Moreover, the oxide scale of high nitrogen steel contained a high concentration of Cr. It is conjectured that, in high temperature oxidation, nitrogen plays a key role in promoting the formation of the oxide scale which has high concentration of Cr, inhibiting oxidation from proceeding. And also it was found that the oxidation resistance of the high nitrogen steels does not depend greatly on Cr content but on their microstructure. The oxidation resistance of high nitrogen ferritic heat-resistant steels increased as the fraction of martensite structure increased. These results indicate for high nitrogen steels Cr diffusion along grain boundaries is further promoted resulting in the formation of protective oxide scale having high Cr concentration. Furthermore as new findings it was confirmed that the Cr diffusion in substrate of steels to form Cr concentrated oxide scale on the metal surface is accelerated by nitrogen while suppressed by carbon in matrix of steel.