Abstract
Mechanical properties (tensile strength and creep) of AlSi10Mg specimens fabricated by selective laser melting (SLM) in the Z-direction were investigated in the 25–400 °C temperature range. Specimens were tested after stress relief treatment. The results revealed that yield stress (YS) significantly decreases and the elongation increases at temperatures higher than 200 °C. The ultimate tensile stress (UTS) continuously decreases with temperature. The creep parameters, namely stress exponent n and apparent activation energy Q, were found to be 25 ± 2 and 146 ± 20 kJ/mole, respectively. It was shown that plastic deformation during creep is governed by dislocation movements in primary aluminum grains. The tested material is actually an aluminum composite reinforced by sub-micron Si particles. The creep resistance of AlSi10Mg alloy fabricated by selective laser melting is close to that for aluminum matrix particles reinforced composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.