Abstract
ABSTRACT The current investigation's objective was to assess the air jet erosion tester's ability to measure the erosive behaviour of plasma sprayed coatings on titanium-15 alloy. 65% NiCrAlY, 30% Cr2O3, and 5% YSZ make up the coating's chemical composition. A study of microstructure and phases was carried out. Microhardness and adhesive strength have both been measured in this work. With impact angles of 30° and 90° at 300°C, 500°C, and 700°C, Al2O3 erodent was utilised in a solid particle erosion test. An optical profilometer was used to calculate the erosion volume loss. The coating erosion resistance was found to be higher than the substrate sample for the test temperature that was employed, and this was more obvious at higher impact angles and higher temperatures The ductile character of the coating is seen in the contour of the deteriorated coating surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.