Abstract

This article describes the design principles deployed in developing high-strength and ductile Mg–Zn–Zr–Ca–Mn(–Yb) alloys based on a concept, which aims to restrict grain growth considerably during alloy casting and forming. The efficiency of the development approach is discussed. Moreover, the microstructure and phase analysis of the alloys subjected to different thermal treatments are presented and the influence of the alloy composition, particularly the addition of Yb, on the evolution of the microstructure is discussed in connection with the mechanical properties of the materials. The newly developed alloys exhibit high strength (yield stress of up to 350MPa) at considerable ductility (elongation to fracture of up to 19%) in the as-extruded state and reveal age hardening potential (increase in hardness of 10–15% compared to that in the recrystallization heat-treated state). Appropriate heat treatments enable tailoring of the strength–ductility relation. Thermal annealing of the material resulted in a remarkable increase in ductility (elongation to fracture of more than 20% for all heat-treated samples) while high strength is retained (yield stress ranging from 210 to 315MPa). We attribute the attractive mechanical properties of the developed alloys to their fine-grained microstructure, where the grain boundaries and lattice defects are stabilized by second phase particles formed during casting and thermal treatments.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.