High Strength Concrete Matrix for Textile Reinforced Concrete Production in Special Curing Conditions

Abstract

This contribution deals with interesting and progressive curing method applied to fresh concrete matrix for textile reinforced concrete production. The application of high pressure 0.3 MPa and temperature 130 °C in 100 % humidity environment for 4 hours was performed. Cement matrix and steel fibers reinforced cement matrix has been investigated. The goal of this research is to quantified compressive strength, flexure strength, bulk density and dynamic modulus of elasticity of both mixtures. These parameters were investigated after hydrothermal curing process at the ages 6, 12, 15, 18, 21 and 24 hour after first contact of water with cement. All parameters were investigated on specimens 40 x 40 x 160 mm3 and the destructive tests were controlled by increase of deformation. Special curing condition led to an increase of the compressive strength by more than 10 % in case of cement matrix, and by more than 40 % in case of fiber reinforced cement matrix.