Abstract
A combination of high strength and good ductility was achieved in a precipitation hardenable Cu-3Ag-0.5Zr alloy through cryo-rolling (80% reduction in thickness) and aging in the temperature range (200-500 °C). The high-strength sheets produced by cryo-rolling showed a threefold increase in yield strength compared to that of the solution-treated and aged (220 MPa) sample, while retaining good ductility. An optimum combination of high strength (614 MPa) and ductility (8%) was achieved by 80% cryo-rolling and aging at 320 °C for 1 h. The high strength and good ductility obtained was attributed to various microstructural factors such as deformation twins, ultra-fine grains, high dislocation density and fine nano-sized silver precipitates.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.