Abstract
The fine-grained duplex stainless steel Fe-22Cr-5Ni-3Mo-0.3N consisting of α- and γ-Fe(Cr,Ni,Mo) solid solutions exhibits structural superplasticity at deformation temperatures of 900 to 1050°C. The equiaxed microstructure with an average grain size of d α,γ = 3 μm was produced by thermomechanical processing. This steel shows also superior superplastic properties at high strain rates up to e 5.10 -2 s -1 . Maximum strain rate exponents of m = 0.5 and elongations to failure of more than 800% were achieved. The superplastic deformability (m > 0.3) of this steel in a wide strain rate range enables near net shape deep drawing or blow forming of parts with complex shape applying low flow stresses. A deformation model is presented to describe the superplastic behaviour at high strain rates. Grain and interphase boundary sliding is accommodated by sequential steps of dislocation glide and climb. The maximum m-value of about 0.5 and an activation energy of 260 kJ/mol, which is comparable to that of self diffusion of iron in γ-Fe (270 kJ/mol), and high dislocation densities indicate that dislocation climb in the slightly solid solution hardened γ-Fe phase (solid solution class II type of material) is the rate controlling step for superplastic flow.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.