Abstract
A dynamic impact test was performed on as-rolled AZ31 alloys with gradient microstructure under various strains. The microstructural evolution and mechanical properties were systematically investigated. As the strain rate gradually increased, an increasing number of twins were formed, facilitating dynamic recrystallization (DRX), and the mechanical properties were also gradually improved. The microstructure became heterogeneous at higher strain rates, but the peak stress decreased. The impact process resulted in a significantly higher performance due to microstructural refinement, work hardening by dislocations, and precipitates. In addition, both the adiabatic shear band and the adjacent crack experienced a temperature rise that exceeded the recrystallization temperature of the alloys. This observation also explains the presence of ultrafine recrystallized grains within the adiabatic shear band and the appearance of molten metal around the crack.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.