Abstract
ABSTRACTSingle-crystal specimen of high-temperature superconductor Bi2Sr2CaCu2Ox was irradiated with 3.5 GeV Xe ions at room temperature up to 1.0 × 1011 ion/cm2. Significant enhancement of magnetization by the irradiation was confirmed. The irradiated specimens were studied by using a high-resolution transmission electron microscope with field emission electron gun (FE-TEM), and, also, with an energy dispersive x-ray analyzer (EDS). Columnar defects with diameter of about 6 nm were observed along the incident ion tracks. By nanoscale high-resolution x-ray spectrochemical analysis across the columnar defect, enrichment of Cu and depletion of Bi, Sr and Ca in the columnar defect center, and vice versa in the outskirts of the defect, was found for the first time. Oxygen depletion in the defect, and increased distribution outside of the defect were also found by electron energy loss spectroscopy. This experimental evidence suggests that the columnar defects are formed as a consequence of Coulomb explosion induced by the electronic excitation of the high-energy heavy ions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.