Abstract
The home-designed metal organic chemical vapor deposition (MOCVD) system was applied to prepare the Gd0.5Y0.5Ba2Cu3O7-δ (GdYBCO) films at a high deposition rate in order to improve the production efficiency and reduce the preparation cost of high temperature superconducting tapes. Based on a simple self-heating method, the distance between the shower head and the substrate surface can be reduced effectively to increase the concentration of metal organic sources on the substrate surface, which can commendably improve the deposition rate of GdYBCO films and the utilization ratio of metal organic sources. At last, the GdYBCO films were successfully prepared on the LaMnO3 template at the high deposition rate of 1 μm/min by the MOCVD process based on the simple self-heating method and the critical current (Ic) was more than 220 A/cm-width (77 K, 0 T), corresponding to the critical current density (Jc) more than 4.4 MA/cm2 (77 K, 0 T).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.