Abstract
Using fast time‐resolved in situ X‐ray diffraction, charge‐rate dependent phase transition processes of layer structured cathode material LiNi1/3Mn1/3Co1/3O2 for lithium‐ion batteries are studied. During first charge, intermediate phases emerge at high rates of 10C, 30C, and 60C, but not at low rates of 0.1C and 1C. These intermediate phases can be continuously observed during relaxation after the charging current is switched off. After half‐way charging at high rate, sample studied by scanning transmission electron microscopy shows Li‐rich and Li‐poor phases' coexistence with tetrahedral occupation of Li in Li‐poor phase. The high rate induced overpotential is thought to be the driving force for the formation of this intermediate Li‐poor phase. The in situ quick X‐ray absorption results show that the oxidation of Ni accelerates with increasing charging rate and the Ni4+ state can be reached at the end of charge with 30C rate. These results give new insights in the understanding of the layered cathodes during high‐rate charging.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.