Abstract
Composite ceramics based on the spinel Mg2TiO4 were prepared by a conventional mixed‐oxide route. To achieve the temperature stabilization of the dielectric constant, each of the composites was added with 7 mol% CaTiO3. The effect of the substitution of isovalent Co for Mg on the microstructure and the microwave dielectric properties of the composite ceramics was also investigated. A maximum Q×f value of around 150–160 THz was obtained for the undoped Mg2TiO4, whereas a reduced Q×f value was observed for an increase in the Co concentration in the system (1−x)Mg2TiO4−xCo2TiO4. Upon doping with 7 mol% CaTiO3, the Q×f value passed through a maximum with increasing Co concentration. Adding ZnO–B2O3 to the composite system based on Co‐doped Mg2TiO4 resulted in a reduction of the sintering temperature by 150°–200°C without any significant degradation in the Q×f value.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.