Abstract
Pb0.87Ba0.1La0.02(Zr0.7Sn0.24Ti0.06)O3 antiferroelectric ceramics with high pyroelectric response were first prepared at a temperature as low as 1000°C using PbO–B2O3 glass. The result showed that suitable PbO content in PbO–B2O3 glass was good for the improvement of electrical properties of antiferroelectric ceramics. Besides, it was observed that with the increase of sintering time, the AFE phase was gradual instable, which was attributed that B3+ with small ions radius replacing Ti4+ with large ions radius caused the increase of tolerance factor of antiferroelectric ceramics, and the dielectric peak became steep due to the decrease of glass content with small dielectric constant. Further, The maximum pyroelectric coefficient of 9050μC/m2K and maximum figure of merit of 20.7×10−5Pa−0.5 were obtained in Pb0.87Ba0.1La0.02(Zr0.7Sn0.24Ti0.06)O3 antiferroelectric ceramics with 1wt% 0.8PbO–0.2B2O3 glass sintered at 1000°C for 12h, which are comparable with that of phase transition pyroelectric materials BST and BZT sintered at as high as 1300°C. Our results open up the way to low-temperature sintering of PZST based antiferroelectric ceramics with high pyroelectric response and provide a basis for antiferroelectric materials used in thick-film based uncooled infrared detector.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.