Abstract
A high-pressure hot-pressing process was applied to densify a commercial boron carbide-titanium diboride (B4C-TiB2) powder mixture. Nearly fully dense (98.6%) materials were obtained at 1 700 °C under a pressure of 100 MPa. Compared to the sintering temperature required to achieve similar results when a pressure of only 30 MPa was applied, the sintering temperature was found to decrease by about 200 °C under pressure of 100 MPa. Analysis of the thermodynamics and microstructure showed that the plastic deformation of the B4C grains induced by high pressure dominated the densification mechanism when high pressure was applied. Furthermore, higher pressure resulted in remarkably improved mechanical properties of the composites, which could be traced back to the generation of stacking faults in the B4C grains and aggregation of TiB2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.