Abstract
High-pressure rheology has been used to assess the effects of supercritical carbon dioxide (scCO2) on the melting point (Tm) and viscosity of poly(ε-caprolactone) (PCL) over a range of temperatures and pressures up to 300 bar over a wide range of shear rates. Plots of the storage and loss moduli against temperature show a significant shift of Tm to lower temperatures in the presence of CO2, indicating that the polymer crystals melt at temperatures much lower than the ambient pressure Tm.Furthermore, a significant decrease in the viscosity of two PCL grades with different molecular weight (Mn ∼ 10 kDa and 80 kDa) was also detected upon increasing the CO2 pressure to 300 bar. Experimental viscosity data were fitted to the Carreau model to quantify the extent of the plasticising effects on the zero-shear viscosity and relaxation time under different conditions. Similar analyses were conducted under high-pressure nitrogen, to compare the effects obtained in the presence of a non-plasticising gas.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.