Abstract
Abstract Ti—6Al—4V alloy powder was processed by electrode induction melting gas atomization (EIGA) at high gas pressure (5.5–7.0 MPa). The effects of atomizing gas pressure on the powder characteristics and the microstructure, along with the mechanical properties of the as-fabricated block by laser melting deposition (LMD), were investigated. The results indicate that the diameters of powders are distributed in a wide range of sizes from 1 to 400 μm, and the median powder size (d50) decreases with increasing gas pressure. The powders with a size fraction of 100–150 μm obtained at gas pressures of 6.0 and 6.5 MPa have better flowability. The oxygen content is consistent with the change trend of gas pressure within a low range of 0.06%–0.20%. Specimens fabricated by LMD are mainly composed of α+β grains with a fine lamellar Widmanstatten structures and have the ultimate tensile strength (UTS) and yield strength of approximately 1100 and 1000 MPa, respectively. Furthermore, the atomized powders have a favorable 3D printing capability, and the mechanical properties of Ti—6Al—4V alloys manufactured by LMD typically exceed those of their cast or wrought counterparts.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.