Abstract
AbstractWe are examining various spinel-structured thin films (e.g., Cd2SnO4, Zn2SnO4) to develop higher-quality transparent conducting oxides (TCO) than more conventional materials such as indium tin oxide. Here, we report on cadmium indate (CdIn2O4, CIO), which is another member of this family. Thin films of CIO were deposited by radio-frequency (RF) magnetron sputtering, from an oxide target, onto borosilicate glass substrates. The variables included the substrate temperature, sputtering gas composition, and pressure. Film properties were measured before and after heat treatment. Characterization involved Hall effect measurements, optical and infrared spectrophotometry, X-ray diffraction, and atomic-force microscopy. Film resistivities as low as 2.3x10-4Ω cm were achieved for a film thickness of 0.55 μm. The transmittance was 90% in the visible region of the spectrum, without correction for substrate losses and without an anti-reflection coating. The plasma resonance occurred at longer wavelengths than for other materials and this, with a bandgap of approximately 3.1 eV, presents a wide window for optical transmittance. The highest mobility was 54 cm2 V-s-1 and the highest carrier concentration was 7.5x1020 cm-3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.