Abstract
High performance oxidation resistant Si-SiC coating for C/C composites was prepared by a two-step pack cementation method using silicon, graphite powders as source materials and Al2O3, MgO, B2O3 as additives. XRD analyses revealed that the obtained coating was composed by β-SiC, Si and α-SiC; SEM analyses displayed that the as-prepared coating exhibited dense surface and cross-section microstructures. Isothermal oxidation test in air at 1773 K showed that the weight loss of the as-obtained Si-SiC coating coated sample after 200h was only 4.42 × 10–4 g.cm–2. The main cause of the weight loss of the coated sample after long time oxidation is due to the vaporization and exhausting of SiO2 glass film which could not provide sufficient glass phase to seal the holes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.