Abstract
In this paper, biobased and environmentally friendly rigid polyurethane foams (RPUF) from high hydroxyl value castor oil-based polyols have been prepared without the addition of petroleum-based polyols in the formulation. The new Biopolyol with high hydroxyl value was designed on the basis of the analysis of functionality, structure and hydroxyl value relation and synthesized directly from castor oil in a facile one-pot three-step system. A series of Biopolyols with hydroxyl values in the range of 550–650 mg KOH/g were obtained through transesterification, epoxidation, and hydrolysis. The Biopolyol chemical structure was characterized using FT-IR,1H NMR spectroscopies. The formulated blend polyol with amine catalysts and cyclopentane as a blowing agent have good cyclopentane solubility and phase separation between cyclopentane and polyol was not observed after 30 days. The foaming characteristics were evaluated and improved results were obtained. The thermal conductivity, thermal stability, compressive strength, morphology, dimensional stability, density, and foam flow of the RPUFs were characterized. The results are compared with RPUF prepared using standard commercial polyether polyols for pour-in-place RPUFs. The prepared biobased RPUFs from Biopolyol was able to reach the required satisfactory properties for the appliance industry.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.