Abstract
AbstractThis work reports on the energy transfer efficiency for Nd3+/Yb3+ co‐doped tellurite glasses (80TO2‐20WO3, in mol%,). The correlation between Yb3+ ion concentration and the downconversion mechanism was investigated using optical and thermal lens spectroscopies, which enabled investigation of the radiative and nonradiative processes, respectively, involved in energy transfer from neodymium to ytterbium. The Nd3+ near‐infrared fluorescence disappeared almost entirely when the maximum concentration of Yb3+ ions (4 mol%) was doped into the host. In contrast, there was a corresponding increase in the ytterbium emission at around 980 nm. When ytterbium was added, there was also a simultaneous reduction in the amount of heat generated by the sample due to a reduction in the nonradiative decay rate, corroborating the suspected high energy transfer efficiency of Nd3+→Yb3+. The results indicate that tungsten‐tellurite glasses may be of potential use in solar cells for matching the solar emission spectrum to the semiconductor cell.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.