High-Modulus Wholly Aromatic Fibers. I. Wholly Ordered Polyamide-Hydrazides and Poly-1,3,4-oxadiazole—Amides

Abstract

Abstract Several completely ordered polyamide-hydrazide copolymers were prepared via low temperature poly condensation of aromatic diacid chlorides with symmetrical aromatic diamines containing preformed dihydrazide linkages. Highly crystalline, hot-drawn fibers of the polyamide-hydrazide containing only para-oriented phenylene units showed unusually high strength and exceptionally high initial modulus: 10.8 and 508 g/den, respectively, at 2.9% elongation-to-break. The as-spun fibers also exhibited rather high tensile strength and unusually high initial modulus: 8.2 and 291 g/den, respectively, at 9.4% elongation-to-break. The hot-drawn fiber retained considerable strength at elevated temperatures, exhibiting a tenacity of 1.4 g/den and an initial modulus of 169 g/den at 350°C. Heat-aging of the as-spun fiber at 185°C in air showed that 66% of the original tenacity, 41% of the elongation, and 86% of the modulus were retained even after 336 hr. Substitution of as little as 25 mole % meta-oriented phenylene...