High gain ultraviolet photodetectors based on AlGaN/GaN heterostructures for optical switching

Abstract

We report on the optoelectronic properties of Al0.25Ga0.75N/GaN-based ultraviolet (UV) photodetectors for the application as a high current, high gain optical switch. Due to an internal gain mechanism combined with the high conductivity of the two-dimensional electron gas at the heterostructure interface, photocurrents in the milliampere-range were obtained with UV illumination. By employing a mesa structure design with meander geometry very low dark currents below 50 nA up to a bias voltage of 100 V were achieved. Optical switching with an on/off-current-ratio of five orders of magnitude was demonstrated. The response time was determined to be 6 ms and persistent photoconductivity was observed. The photodetector is visible-blind with a cut-off wavelength of 365 nm according to the band gap energy of the GaN absorption layer. A high responsivity with a maximum of 70 A/mW at 312 nm and 100 V bias voltage was demonstrated.