Abstract
With increased public awareness of fire-safety, flame retardant materials have been widely used and developed. Among them, a polyester called CPET, synthesized by the copolymerization of polyethylene terephthalate and 2-carboxyethyl (phenyl) phosphinic acid, has a good fire-safety and has been employed in the manufacture of synthetic fibers. However, the fabricated fiber made of CPET simultaneously possessing good flame retardancy and mechanical properties is a dilemma. Herein, we resolve this problem through the reactive blending of CPET with a type of thermotropic liquid crystal copolyester (PPDT) and subsequently solid-state polymerization (SSP). Thus, the fire-safety of the CPET/PPDTSSP blend improves greatly. The peak heat release rate, total heat release, and total smoke release decrease by 31.2%, 16.3%, and 11.0%, respectively, compared with those of CPET. Meanwhile, the CPET/PPDTSSP shows better crystallization and mechanical properties than CPET. The strength at yield and Young’s modulus of CPET/PPDTSSP increase by 20.0% and 15.8%, respectively. This blend shows great potential in the fabrication of fire-safety fibers with high strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.