Abstract
Electrostatic dielectric capacitors have received great attention due to their ultrafast charging-discharging speed and ultrahigh power density. However, the low energy storage density and efficiency are the main obstacles to their practical applications. In this work, solid solution relaxor ceramics with different proportions of lead-free ferroelectrics Ba0.5Sr0.5TiO3 (BST) and K0.5Na0.5NbO3 (KNN) were prepared. Superior energy storage performance was achieved in the 0.7BST-0.3KNN ceramics with a breakdown strength (Eb) of 510 kV/cm, a recoverable energy storage density (Wrec) of 4.10 J/cm3, and an energy storage efficiency (η) of 80 %, which was fairly stable over the temperature range of 30–100 °C. Since multiple cations with different valence and radius coexist on the equivalent sites (A or B sites) of the solid solutions, the chemical disorder and the corresponding lattice distortion induced the coexistence of cubic, tetragonal, and orthorhombic phases, as well as the appearance of the multiphase polar nanoregions (PNRs), making the ferroelectric hysteresis loops linear. At the same time, ultrafine grains in the ceramics greatly improved the Eb. For achieving excellent energy storage performance, this work demonstrates a potential candidate of (1-x)BST-xKNN lead-free solid solution ceramics and a combined strategy of fine grains and multiphase PNRs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.