Abstract
An optimum composition range (29%≤ x≤31%) of 〈001〉 oriented (1− x)Pb(Mg 1/3Nb 2/3)O 3– xPbTiO 3(PMNT) crystals was ascertained for multilayer actuator applications, which exhibited high-strain and low-hysteresis behavior. A −1.5 kV/cm negative E-field can be applied to PMNT ferroelectric samples with low hysteresis. Forty layer actuators with individual element sizes of 7×7×0.7 mm 3 were fabricated under identical processing conditions using two different materials: (1) single crystal PMNT and (2) commercial PZT-SF ceramics. Under free-load conditions, 48 μm displacements can been achieved in PMNT actuators at electric fields ranging from −1.5 to 10 kV/cm, which is more than twice the displacement of the PZT-SF actuators driven from −10 to 10 kV/cm. Under 4 kg loading, the displacements in PMNT stain actuators are decreased to 42.5 μm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.