Abstract
To successfully develop a regioregular polymer, poly[4,8‐bis(5‐(2‐hexyldecyl)thiophen‐2‐yl)benzo[1,2‐b:4,5‐b′]dithiophene][5,5′‐bis(7‐(4‐(2‐butyloctyl)thiophen‐2‐yl)‐6‐fluorobenzo[c][1,2,5]thiadiazol‐4‐yl)‐2,2′‐bithiophene] (PDBD‐FBT), a symmetric monomer synthesized in high yield by tin homo‐coupling reactions. PDBD‐FBT is suitable as a donor material in organic photovoltaics (OPVs) because it shows high crystallinity and strong face‐on packing properties. These properties were amplified by thermal annealing (TA). This causes a power conversion efficiency (PCE) enhancement in PDBD‐FBT‐based OPVs. Using PDBD‐FBT as a polymer donor and 2,2′‐((2Z,2′Z)‐((12,13‐bis(2‐heptylundecyl)‐3,9‐diundecyl‐12,13‐dihydro‐[1,2,5]thiadiazolo[3,4‐e]thieno[2″,3″:4′,5′]thieno[2′,3′:4,5]pyrrolo[3,2‐g]thieno[2′,3′:4,5]thieno[3,2‐b]indole‐2,10‐diyl)bis(methanylylidene))bis(5,6‐difluoro‐3‐oxo‐2,3‐dihydro‐1H‐indene‐2,1‐diylidene))dimalononitrile (Y6‐HU) as an electron acceptor, a PCE of 7.91% was achieved without any additive and TA at optimized active layer film thickness of approximately 100 nm. After TA, a PCE of 12.53% was achieved with a 58% increase compared with the reference devices. Owing to the strong crystallinities, trap‐assisted recombination occurs by excessively formed grain boundaries; however, efficient exciton dissociation sufficiently covers these drawbacks. Even in the approximately 340 nm‐thick film condition, this tendency is more pronounced (73% PCE enhancement is observed from 6.17% to 10.69% of PCE in the without and with TA devices, respectively). Our study demonstrates that it is possible to manufacture thickness‐insensitive OPVs based on regioregular polymers with strong crystallinity and face‐on characteristics, thereby providing a solution to the thickness variation of large‐area organic solar cell modules.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.