Abstract
Niobium carbide (NbC) nanoparticles embedded on the surface of carbon spheres (CS) were synthesized at 1350 °C by the carbothermal reduction of niobium oxide precursor in flowing argon (Nbc@CS). The morphology, crystal structure, and magnetic properties of the hybrid nanocomposite were investigated by means of electron microscopy, X-ray diffraction and a superconducting quantum interference device. It was found that the NbC@CS nanocomposites exhibit type-II superconductivity with a critical temperature (Tc) of 8-12 K, typical for stoichiometric NbC. The superconducting hysteresis loop reveals several interesting traits, including strong vortex pinning, the presence of asymmetry and a high penetration field. Moreover, the sample shows much improved irreversible (Hirr), lower (Hc1) and upper (Hc2) critical fields. The coherence length (ξ), penetration depth (λ), and Ginzburg-Landau (κ) parameters for the sample were estimated to be 9.78 nm, 33 nm and 3.39, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.