Abstract
Red emission with high color purity in Y2Ti2O7:Yb3+,Er3+ material is successfully obtained by high-concentration doping of Yb3+ and Er3+ under 980 and 1550nm excitation based on the special layer structure of pyrochlore crystal. It shows that Yb3+ ion content and excitation wavelength greatly influence the red emission percent of total up-conversion luminescence intensity of Y2Ti2O7:Yb3+,Er3+. Y2Ti2O7:Yb3+,Er3+ shows much better red color purity at 1550nm excitation than at 980nm. Furthermore, the co-doping of Yb3+ ions considerably boosts the red emission under 980 or 1550nm pumping with different luminescence mechanisms compared with Y2Ti2O7:Er3+ sample. The red emission percent of total up-conversion luminescence intensity gradually increases with the increment of Yb3+ concentration at both excitation sources. The red-to-green emission ratio of the sample is 6.97 (980nm) and 23.26 (1550nm) when the Yb3+ content is 30mol%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.