High-κ Dielectric (HfO2)/2D Semiconductor (HfSe2) Gate Stack for Low-Power Steep-Switching Computing Devices.

Abstract

Herein, a high-quality gate stack (native HfO2 formed on 2D HfSe2) fabricated via plasma oxidation is reported, realizing an atomically sharp interface with a suppressed interface trap density (Dit ≈ 5 × 1010 cm-2 eV-1). The chemically converted HfO2 exhibits dielectric constant, κ ≈ 23, resulting in low gate leakage current (≈10-3 A cm-2) at equivalent oxide thickness ≈0.5 nm. Density functional calculations indicate that the atomistic mechanism for achieving a high-quality interface is the possibility of O atoms replacing the Se atoms of the interfacial HfSe2 layer without a substitution energy barrier, allowing layer-by-layer oxidation to proceed. The field-effect-transistor-fabricated HfO2/HfSe2 gate stack demonstrates an almost ideal subthreshold slope (SS) of ≈61 mV dec-1 (over four orders of IDS) at room temperature (300 K), along with a high Ion/Ioff ratio of ≈108 and a small hysteresis of ≈10 mV. Furthermore, by utilizing a device architecture with separately controlled HfO2/HfSe2 gate stack and channel structures, an impact ionization field-effect transistor is fabricated that exhibits n-type steep-switching characteristics with a SS value of 3.43 mV dec-1 at room temperature, overcoming the Boltzmann limit. These results provide a significant step toward the realization of post-Si semiconducting devices for future energy-efficient data-centric computing electronics.