Abstract
X-ray scattering and microtomography (μCT) are useful techniques to reveal the structure of wood at the nano- and micrometer scales. The nanostructure of xylem in greenhouse-grown 2.5- to 3.5-month-old Populus tremula L. × tremuloides Michx. trees was characterized using wide-angle X-ray scattering (WAXS), and the cellular structure was investigated using μCT. For comparison, the nanostructure of wood in 2-year-old silver birch, Norway spruce and Scots pine saplings was determined. Based on the μCT results, the lengths of fiber lumina of the hybrid aspen saplings were shorter than any previous results on the lengths of wood fibers. The mean microfibril angles of the hybrid aspen saplings were significantly lower (8°–14°) than those of the birch, spruce and pine saplings (27°–35°) implicating that cellulose microfibrils were oriented nearly parallel to the cell axis in the young hybrid aspen saplings. Hybrid aspen saplings were found to contain tension wood based on the histochemical analysis and μCT images. However, typical tension wood properties, i.e. larger crystallite width and higher crystallinity than in normal wood, were detected only in a few hybrid aspen samples, while in most of the hybrid aspen saplings, the crystallite widths (3.0 ± 0.1 nm) and the crystallinities (30 ± 5 %) corresponded to those of normal wood. The deformations of cellulose crystallites were determined using WAXS in situ upon dehydration of the never-dried samples. In all the species studied, the cellulose unit cell dimension decreased and disorder of cellulose chains increased parallel to the chains upon drying. Also, the transverse disorder of chains increased in birch, spruce and pine, while no changes were detected in this direction in hybrid aspen. The crystallite widths and drying deformation results might indicate that the gelatinous layer has not fully developed in the young hybrid aspen saplings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.