Abstract
The irradiation creep behavior of F82H and several JLF-1 steels has been measured at 573 and 773 K up to 5 dpa using pressurized creep tubes irradiated in HFIR. These tubes were pressurized with high-purity helium to hoop stress levels of 0 to 400 MPa at the irradiation temperature. The results for F82H and JLF-1 with hoop stress of 400 MPa showed small creep strains (<0.25%) after irradiation at 573 K. The irradiation creep strain at 573 K in these steels is linearly dependent on the applied stress at stress levels below 250 MPa. However, at higher hoop stress levels, the creep strain is nonlinear. At 773 K, the irradiation creep strain of F82H is linearly dependent on the applied hoop stress level below 100 MPa. At higher stress levels, the creep strain increased strongly. The creep compliance co-efficient for F82H and JLF-1 is consistent with the values obtained for other steels. These data contribute to the materials database for ITER test blanket design work.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.