Abstract
Single and dual-beam self-ion irradiations were performed at 500 °C on ultra-high purity Fe14%Cr alloy to ~0.33 displacements-per-atom (dpa), and 0 or 3030 atomic-parts-per-million (appm) helium/dpa, respectively. Using transmission electron microscopy, we reveal that helium can drastically modify the dislocation loop Burgers vector in Fe-Cr alloys. Helium co-implantation caused complete disappearance of a/2 type dislocation loops, and the microstructure consisted of only a loops. Conversely, a/2 type loops were predominant without He co-implantation. The total loop density remained largely unaffected. The results strikingly contrast literature asserting that helium stabilizes a/2 type loops in bcc Fe alloys, based on low temperature irradiations. Collectively analyzing the results with literature suggests that the small positive interaction between helium and self-interstitial atoms (SIA) in Fe, predicted by atomistic simulations, maybe insufficient to holistically explain the dislocation loop microstructure development in presence of helium. Helium-SIA positive binding inadvertently implies elevated a/2 loop fraction and higher loop densities that the present results contradict. Helium induced high cavity density causing a preferential loss of highly glissile clusters, leaving the matrix saturated with type clusters is proposed as a potential mechanism. Further, the in-situ irradiations combined with Burgers vector analysis strengthened the evidence of Cr-induced dislocation loop mobility reduction that appears to stabilize the a/2 type loops and causes higher loop densities in Fe-Cr alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.