Heat Treatment Optimization Studies on PIT ${\rm Nb}_{3}{\rm Sn}$ Strand for the NED Project

Abstract

For the Next European Dipole (NED) program, a Powder-In-Tube (PIT) strand was successfully developed by SMI. This high-performance Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn strand presents a non-copper critical current density of ~ 2500 A/mm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> at 12 T applied field and 4.2 K and a filament diameter around 50 mum. Extensive heat treatment optimization studies were performed in order to maximize both critical current and RRR, with a plateau temperature down to 625degC and duration up to 400 hours. It appears that a critical current enhancement of ~ 10% can be achieved for a reaction schedule of 320 hours at 625degC with non-copper critical current density respectively exceeding 2700 and 1500 A/mm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> at 12 and 15 T (4.2 K). Thanks to this modified heat treatment, this strand completely fulfills the NED stringent specification.