Abstract
A selective laser-melted Al-Mn-Sc alloy with 99.9% relative density has been obtained in this work through systematic process optimization. The as-fabricated specimen had the lowest hardness and strength, but the highest ductility. The aging response has shown that 300 °C/5 h is the peak aged condition, and it had the highest hardness, yield strength, ultimate tensile strength, and elongation at fracture. Such a high strength was attributed to the uniformly distributed nano-sized secondary Al3Sc precipitates. A further increase in aging temperature to 400 °C resulted in an over-aged condition, which contained a reduced volume fraction of secondary Al3Sc precipitates and resulted in a reduced strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.