Abstract
Heat treatments of a hot dip galvanizing TRIP (Transformation induced plasticity) steel with chemical composition 0.20C-1.50Mn-1.2Al-0.07P(mass%) were performed in a Gleeble 3500 laboratory equipment. The heat treatment process parameters were varied to investigate the effect of intercritical annealing temperature as well as isothermal bainitic transformation (IBT) temperature and time, on the microstructure and the mechanical properties. The microstructure was investigated using scanning electron microscopy, transmission electron microscopy and x-ray diffraction, while mechanical properties were evaluated by tensile testing. Furthermore, to generate a better understanding of the phase transformations during heat treatment, dilatometry trials were conducted. The desired microstructure containing ferrite, bainite, retained austenite and martensite was obtained after the heat treatments. It was further found that the IBT is critical in determining the mechanical properties of the steel, since it controls the fraction of bainite. With increasing bainite fraction, the fraction of retained austenite increases while the fraction of martensite decreases. The mechanical properties of the steel are excellent with a tensile strength above 780MPa (expect in one case) and elongation above 22%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.