Abstract
This study investigates the effect of heat treatment on changes in microstructure and wear behaviour of WC-NiCr coatings. Two feedstock powders with a similar chemical composition and different particle sizes (near nano-structured WC-17NiCr and microstructured WC-15NiCr) were used. High-velocity oxyfuel spraying technique was used to deposit coatings on to a mild steel substrate using identical spraying parameters. Coated samples were then heat treated in a nitrogen atmosphere at 500 and 700°C. The effect of heat treatment on changes in hardness and wear performance of the coatings was studied using microstructural analysis, micro-hardness indentation and abrasive wear tests. The results showed that the heat treatment increased the hardness of both coatings and a corresponding increase in wear resistance was recorded. The formation of a brittle CrWO4 phase in the microstructured coating resulted in brittle fracture of the coating and this gave lower wear resistance compared to the nanostructured coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.