Abstract The influence of heat treatment on the microstructure, mechanical properties, and wear behaviors of stainless steel 316L (SS316L) produced via selective laser melting (SLM) was investigated. The fabricated SLM samples were subjected to two different heat treatments: a typical furnace-type heat treatment conducted at 1100 °C for 0.5 h and hot isostatic pressing performed at 1100 °C and 100 MPa for 1.5 h. High-density SLM samples with low porosities were obtained by increasing the laser power and decreasing the scan speed. The heat treatments of the fabricated SLM samples induced the removal of porosity, cellular microstructure, and dense dislocation structures with a slight increase in grain size. In terms of mechanical properties, the fabricated SLM samples exhibited similar hardness and tensile strength properties to those of the conventional SS316L, while a significantly lower elongation was evident. The heat treatments of the fabricated SLM samples improved elongation, while the surface hardness and tensile strength decreased owing to microstructural evolution. During the pin-on-disk test, the conventional SS316L and fabricated SLM sample exhibited similar wear resistance values, which decreased after the heat treatments of the fabricated SLM samples owing to the heat treatment-induced surface softening.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.