Abstract
To evaluate the influence of various photoactivation techniques on the internal gap, Knoop-hardness, and polymerization depth of silorane- and methacrylate-based composites in Class II restorations. Preparations were made in third molars (n = 10), according to composites (Filtek P60: methacrylate; Filtek P90: silorane) and photoactivation techniques (OC: occlusal photoactivation (control); OBL: occlusal+buccal+lingual photoactivation; and BLO: buccal+lingual+occlusal photoactivation (transdental)). Composites were inserted in two increments, both individually photoactivated for 20s. After 24h, specimens were sectioned and the ratio of internal gaps to interface length (%) recorded. Hardness was tested across the transversal section of restorations (1-4 mm below the surface). Silorane restorations showed significantly lower gaps compared with methacrylate, regardless of polymerization technique (P<.05). Supplementary energy dose in OBL and BLO protocols caused significant increase in gaps in silorane restorations (P<.05). For methacrylate restorations, OBL activation caused significantly higher gap formation (P<.05). Significantly lower hardness values were seen for silorane than for methacrylate composites (P<.05), regardless of depth and photoactivation. Significantly higher hardness values were seen in BLO activation for methacrylate restorations compared with control (P<.05); for silorane, no differences were observed. Significantly higher hardness values were observed at 1 and 3 mm compared to 2 and 4 mm for both composites. Internal gaps and hardness are affected by composite type and photoactivation. Despite the reduced values, hardness of silorane is not influenced by photoactivation or by depth. Internal gaps are dependent on the energy dose for both composites, with silorane showing lower internal gaps.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.