Hardness, Microstructure, and Residual Stresses in Low Carbon Steel Welding with Post-weld Heat Treatment and Temper Bead Welding

Abstract

This paper investigates the effects of post-weld heat treatment (PWHT) and temper bead welding (TBW) on hardness, microstructure and residual stresses in multi-layer welding on low carbon steel specimens made with two different weld geometries, viz. (1) smooth-contoured and (2) U-shaped. It was found that the PWHT technique gave overall lower hardness than the TBW technique, but the hardness values in both techniques were acceptable. Microscopy analysis showed that the TBW technique was more effective in tempering the heat affected zone as the grain size decreased slightly at the fusion line in spite of the higher temperature at the fusion line. Residual stresses measured using the hole-drilling method showed that the residual stress is not reduced below yield stress near the last bead solidified in TBW. Only PWHT gives low residual stress results in this area. High tensile residual stresses may result in sensitivity to fatigue loading.