Abstract
The hardness, elastic modulus, and structure of several amorphous carbon films on silicon prepared by cathodic-arc deposition with substrate pulse biasing have been examined using nanoindentation, energy loss spectroscopy (EELS), and cross-sectional transmission electron microscopy. EELS analysis shows that the highest sp3 contents (85%) and densities (3.00 g/cm3) are achieved at incident ion energies of around 120 eV. The hardness and elastic modulus of the films with the highest sp3 contents are at least 59 and 400 GPa, respectively. These values are conservative lower estimates due to substrate influences on the nanoindentation measurements. The films are predominantly amorphous with a ∼20 nm surface layer which is structurally different and softer than the bulk.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.