Abstract

ABSTRACTLead zirconate titanate thin films offer considerably larger piezoelectric coefficients than do ZnO, and so are attractive for microelectromechanical sensors and actuators. To date, much of the research in this field has concentrated on undoped PZT. In this work, PZT films grown from both hard and soft PZT targets have been deposited on platinum coated silicon wafers by pulsed laser deposition so that the effect of doping on the properties can be determined. Dielectric constants of 1000–1500 are regularly achieved in both types of films, with loss values varying from 0.01 for soft films to 0.03 for hard films. Remanent polarizations are typically 30 μC/cm2 for both types of films with no observable difference in coercive fields. When subjected to ∼140 MPa of biaxial tension and compression, only small (∼5%) reversible changes were observed, indicating a lack of substantial domain reorientation in the films.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.