Abstract
We report a new industrial application of aluminum magnesium boride AlMgB14 (BAM) coatings to enhance the hardness of tungsten carbide ceramic (WC-Co) and high-speed steel tools. BAM films were deposited by RF magnetron sputtering of a single dense stoichiometric ceramic target onto commercial WC-Co turning inserts and R6M5 steel drill bits. High target sputtering power and sufficiently short target-to-substrate distance were found to be critical processing conditions. Very smooth (6.6 nm RMS surface roughness onto Si wafers) and hard AlMgB14 coatings enhance the hardness of WC-Co inserts and high-speed R6M5 steel by a factor of two and three, respectively. Complete coating spallation failure occurred at a scratch adhesion strength of 18 N. High work of adhesion and low friction coefficient, estimated for BAM onto drill bits, was as high as 64 J/m2 and as low as 0.07, respectively, more than twice the surpass characteristics of N-doped diamond-like carbon (DLC) films deposited onto nitride high-speed W6Mo5Cr4V2 steel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.