Abstract
H2O2 formation on Pt/C catalyst and Pt1Run/C (n = 1/3, 1/2, 1, 3/2, 2) catalysts was studied with rotating ring-disk electrode (RRDE) in 0.5 M H2SO4. H2O2 formation on Pt/C catalyst and Pt1Run/C catalysts with smaller Ru content increased sharply below 0.1 V vs. RHE. On the other hand, for larger Ru content catalysts, Pt1Run/C (n = 1, 3/2, 2), their H2O2 formation was lower than that of smaller Ru content catalysts below 0.1 V vs. RHE. Pt1Run/C catalysts with larger Ru content prevented H2O2 formation in anode catalyst layer and mitigated membrane degradation in PEFC. Potential cycles between 0.1 V and 1.0 V and between 0.1 V and 1.2 V vs. RHE were applied for Pt1Ru2/C catalyst. H2O2 formation below 0.1 V vs. RHE increased after potential cycles. Ru dissolution from Pt1Ru2/C catalyst was considered to promote H2O2 formation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.