Growth, thermal properties, and LD-pumped 1066 nm laser performance of Nd^3+ doped Gd/YTaO_4 mixed single crystal

Abstract

A new laser crystal Nd:Gd0.69Y0.3TaO4 (Nd:GYTO) with high quality was grown by Czochralski method. The physical properties, including temperature dependent density, specific heat, thermal expansion coefficient, and thermal conductivity, were systematically characterized. The maximum absorption cross section at 809 nm and the stimulated emission cross section at 1066.6 nm are 6.886 × 10−20 cm2 and 22 × 10−20 cm2, respectively. The fluorescence lifetime is measured to be 182.4 μs. Up to 2.37 W of continuous wave (CW) laser operating at 1066.5 nm has been successfully realized, corresponding to an optical conversion efficiency of 36.5% and a slope efficiency of 38%. Compared with Nd:GdTaO4, Nd:GYTO shows an enhancement of the laser performance. These results demonstrate that Nd:Gd0.69Y0.3TaO4 is a novel laser crystal with low symmetry and has great potential as low to moderate power lasers.