We report the growth conditions of nanostructured tungsten oxide (WO 3− x ) thin films using hot-wire chemical vapor deposition (HWCVD). Two tungsten filaments were resistively heated to various temperatures and exposed to an air flow at various subatmospheric pressures. The oxygen partial pressure was varied from 6.0 × 10 −6 to 1.0 mbar and the current through the filaments was varied from 4.0 to 9.0 A, which constitutes a filament temperature of 1390–2340 °C in vacuum. It is observed that the deposition rate of the films is predominantly determined by the oxygen partial pressure; it changes from about 1 to about 36,000 nm min −1 in the investigated range. Regardless of the oxygen partial pressure and filament temperature used, thin films with a nanogranular morphology are obtained, provided that the depositions last for 30 min or shorter. The films consist either of amorphous or partially crystallized WO 3− x with high averaged transparencies of over 70% and an indirect optical band gap of 3.3 ± 0.1 eV. A prolonged deposition time entails an extended exposure of the films to thermal radiation from the filaments, which causes crystallization to monoclinic WO 3 with diffraction maxima due to the (0 0 2), (2 0 0) and (0 2 0) crystallographic planes, furthermore the nanograins sinter and the films exhibit a cone-shaped growth. By simultaneously influencing the surface mobility, by heating the substrates to T surface = 700 ± 100 °C, and the deposition rate, a very good control of the morphology of the deposited films is obtained. Nanowire films, nanocrystallite films and closed crystallite films were thus deposited. These differently nanostructured c-WO 3 films all possess an indirect optical band gap of 2.5 ± 0.1 eV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.