Abstract
The series of (LuBi) <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> Fe <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">5</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">12</inf> film were grown on (111) oriented GGG substrate with diameters 1, 2 and 3 inch by liquid phase epitaxy using Bi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> -base flux. Different types of surface morphology on the grown films were observed. The films' surface was smooth and mirror while the film thickness was less than 13 µm and becomes rough for thickness above this value. The grown films were characterized by measuring magnetization loops and magneto-optic Faraday rotation under magnetization reversal as well as ferromagnetic resonance (FMR). All films with mirror surface demonstrate the in-plane magnetization, high Faraday rotation and FMR linewidth about 0.8 Oe at 9.1 GHz and room temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.