Abstract
ABSTRACTGrowth of single-walled carbon nanotube (SWCNT) was achieved by an alcohol catalytic chemical vapor deposition (CVD) mechanism that was conducted in a high vacuum using Ru catalysts. By optimizing the ethanol pressure, SWCNTs can grow in a wide range of temperature between 500 °C and 900 °C. Both the yield and crystalline quality of SWCNTs reached their maxima at 700 °C. Significantly, the SWCNT growth was achieved even at 450 °C, which was much lower than the growth temperatures that were required for SWCNT growth using Ru catalysts previously. Raman measurements exhibited that the diameter distribution of the SWCNTs that were grown at 450 °C was quite narrow and (11, 4) nanotubes were dominant. The observations of transmission electron microscope (TEM) suggested that the size of the Ru particles were larger than the diameter of SWCNT. Such a relation was similar to the relation observed in the growth of SWCNTs using Pt catalysts.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.