Growth of 2 μm Crack-Free GaN on Si(111) Substrates by Metal Organic Chemical Vapor Deposition

Abstract

A 2 μm high quality crack-free GaN film was successfully grown on 2-inch Si(111) substrates by metal organic chemical vapor deposition with a high temperature AlN/graded-AlGaN multibuffer and an AlN/GaN superlattice interlayer. It is found that the structures, as well as the thicknesses of the multibuffer and interlayer, are crucial for the growth of a crack-free GaN epilayer. The GaN(0002) XRD FWHM of the crack-free sample is 479.8 arcsec, indicating good crystal quality. An AlGaN/GaN heterostructure was grown and tested by Van der Pauw Hall measurement. The electron mobility of two-dimensional electron gas increases from 1928 cm2/V-s to 12277 cm2/V-s when the test-temperature decreases from room temperature to liquid nitrogen temperature. The electron mobility is comparable to that of AlGaN/GaN heterostructures grown on sapphire, and the largest value is obtained for an AlGaN/GaN/Si(111) heterostructure grown by metal organic chemical vapor deposition.